Method and article from aluminum oxide glass and articles made therefrom

ABSTRACT

A method of making an article from an aluminum oxide glass is disclosed. The aluminum oxide glass includes a rare earth oxide. The aluminum oxide glass has a glass transition temperature and a crystallization temperature, and these temperatures differ by at least 25K. The method includes: providing a glass in a form comprising particles, beads, microspheres, or fibers; heating the glass above the T g  such that the particles, beads, microspheres, or fibers coalesce to form a coalesced shape; and cooling the coalesced shape to form the article.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. Ser. No. 10/211,491, filed Aug. 2, 2002, which is a continuation-in-part of U.S. Ser. No. 09/922,526, filed Aug. 2, 2001, now abandoned. This application is related to U.S. 2007/0135290 A1 filed Jan. 15, 2007. This application is also related to U.S. Ser. No. ______ (Attorney Docket No. 56938US018) and U.S. Ser. No. ______ (Attorney Docket No. 56938US019) filed on even date herewith.

FIELD OF THE INVENTION

The present invention relates to a method of making an article by coalescing a plurality of the glass particles. Examples of articles include kitchenware (e.g., plates), dental brackets, and reinforcing fibers, cutting tool inserts, abrasives, and structural components of gas engines, (e.g., valves and bearings).

DESCRIPTION OF RELATED ART

A large number of glass and glass-ceramic compositions are known. The majority of oxide glass systems utilize well-known glass-formers such as SiO₂, B₂O₃, P₂O₅, GeO₂, TeO₂, As₂O₃, and V₂O₅ to aid in the formation of the glass. Some of the glass compositions formed with these glass-formers can be heat-treated to form glass-ceramics. The upper use temperature of glasses and glass-ceramics formed from such glass formers is generally less than 1200° C., typically about 700-800° C. The glass-ceramics tend to be more temperature resistant than the glass from which they are formed.

Although a large number of metal oxides can be obtained in an amorphous state by melting and rapidly quenching, most, because of the need for very high quench rates to provide amorphous rather than crystalline material, cannot be formed into bulk or complex shapes. Generally, such systems are very unstable against crystallization during subsequent reheating and therefore do not exhibit typical properties of glass such as viscous flow. On the other hand, glasses based on the known network forming oxides (e.g., SiO₂ and B₂O₃) are generally relatively stable against crystallization during reheating and, correspondingly, the “working” range where viscous flow occurs can be readily accessed. Formation of large articles from powders of known glass (e.g., SiO₂ and B₂O₃) via viscous sintering at temperatures above glass transition temperature is well known. For example, in the abrasive industry, grinding wheels are made using vitrified bond to secure the abrasive particles together.

It is desirable to provide large articles and/or complex shapes comprising non-traditional glass and glass-ceramics compositions.

SUMMARY OF THE INVENTION

The present invention provides a method of making articles from glass. Optionally, the articles may be a composite of two or more different glass compositions or formulations. In some embodiments the glass is optionally heat-treated to at least partially crystallize the glass.

One embodiment of the present invention provides a method of making an article from glass comprising:

-   -   providing a substrate (e.g., ceramics, metals, intermetallics,         and composites thereof) including an outer surface;     -   providing at least a first glass (e.g., sheets, particles         (including microspheres), and fibers), wherein the first glass         comprises at least two different metal oxides (i.e., the metal         oxides do not have the same cation(s)), wherein the first glass         has a T_(g) and T_(x), and wherein the difference between the         T_(g) and the T_(x) of the first glass is at least 5K (or even,         at least 10K, at least 15K, at least 20K, at least 25K, at least         30K, or at least 35K), the first glass containing less than 20%         by weight SiO₂ (or even less than 15%, less than 10%, less than         5% by weight, or even zero percent, by weight, SiO₂), less than         20% by weight B₂O₃ (or even less than 15%, less than 10%, less         than 5% by weight, or even zero percent, by weight, B₂O₃), and         less than 40% by weight P₂O₅ (or even less than 35%, less than         30%, less than 25%, less than 20%, less than 15%, less than 1%,         less than 5% by weight, or even zero percent, by weight, P₂O₅);     -   heating the first glass above the T_(g) such that at least a         portion of the glass wets at least a portion of the outer         surface of the substrate; and     -   cooling the glass to provide an article comprising ceramic         comprising the glass attached to the at least a portion of the         outer surface of the substrate. In some embodiments, the ceramic         is glass. Optionally, the method can be practiced with a second,         a third, or more, different glass, including glasses having,         respectively, a T_(g) and T_(x), and wherein the difference         between each T_(g) and the T_(x) of a glass is at least 5K (or         even, at least 10K, at least 15K, at least 20K, at least 25K, at         least 30K, or at least 35K), one or more of the additional         glasses optionally contain less than 20% by weight SiO₂ (or even         less than 15%, less than 10%, less than 5% by weight, or even         zero percent, by weight, SiO₂), less than 20% by weight B₂O₃ (or         even less than 15%, less than 10%, less than 5% by weight, or         even zero percent, by weight, B₂O₃), and less than 40% by weight         P₂O₅ (or even less than 35%, less than 30%, less than 25%, less         than 20%, less than 15%, less than 1%, less than 5% by weight,         or even zero percent, by weight, P₂O₅). Preferably the glass, or         if more than one glass is used, at least one of the glasses,         comprises less than 40 percent (preferably, less than 35, 30,         25, 20, 15, 10, 5, or even 0) by weight glass collectively SiO₂,         B₂O₃, and P₂O₅, based on the total weight of the glass.

Another embodiment of the present invention provides a method of making an article from glass comprising:

-   -   providing a substrate including an outer surface;     -   providing at least a first plurality of particles comprising         glass (including glass particles), wherein the glass comprises         at least two different metal oxides, wherein the glass has a         T_(g) and T_(x), and wherein the difference between the T_(g)         and the T_(x) of the glass is at least 5K (or even, at least         10K, at least 15K, at least 20K, at least 25K, at least 30K, or         at least 35K), the glass containing less than 20% by weight SiO₂         (or even less than 15%, less than 10%, less than 5% by weight,         or even zero percent, by weight, SiO₂), less than 20% by weight         B₂O₃ (or even less than 15%, less than 10%, less than 5% by         weight, or even zero percent, by weight, B₂O₃), and less than         40% by weight P₂O₅ (or even less than 35%, less than 30%, less         than 25%, less than 20%, less than 15%, less than 1%, less than         5% by weight, or even zero percent, by weight, P₂O₅);     -   heating the glass above the T_(g) such that at least a portion         of the glass of the first plurality of particles wets at least a         portion of the outer surface of the substrate; and     -   cooling the glass to provide an article comprising ceramic         comprising the glass attached to the at least a portion of the         outer surface of the substrate. In some embodiments, the ceramic         is glass. Optionally, the method can be practiced with a second,         a third, or more, different pluralities of particles comprising         (different) glasses, including glasses having, respectively, a         T_(g) and T_(x), and wherein the difference between each T_(g)         and the T_(x) of a glass is at least 5K (or even, at least 10K,         at least 15K, at least 20K, at least 25K, at least 30K, or at         least 35K), one or more of the additional glasses optionally         contain less than 20% by weight SiO₂ (or even less than 15%,         less than 10%, less than 5% by weight, or even zero percent, by         weight, SiO₂), less than 20% by weight B₂O₃ (or even less than         15%, less than 10%, less than 5% by weight, or even zero         percent, by weight, B₂O₃), and less than 40% by weight P₂O₅ (or         even less than 35%, less than 30%, less than 25%, less than 20%,         less than 15%, less than 1%, less than 5% by weight, or even         zero percent, by weight, P₂O₅). Preferably the glass, or if more         than one glass is used, at least one of the glasses, comprises         less than 40 (preferably, less than 35, 30, 25, 20, 15, 10, 5,         or even 0) percent by weight glass collectively SiO₂, B₂O₃, and         P₂O₅, based on the total weight of the glass.

Another embodiment of the present invention provides a method of making an article comprising:

-   -   providing at least a first glass and second glass (e.g., sheets,         particles (including microspheres), and fibers), wherein the         first glass comprises at least two different metal oxides,         wherein the first glass has a T_(g1) and T_(x1), and wherein the         difference between the T_(g1) and the T_(x1) is at least 5K (or         even, at least 10K, at least 15K, at least 20K, at least 25K, at         least 30K, or at least 35K), the first glass containing less         than 20% by weight SiO₂ (or even less than 15%, less than 10%,         less than 5% by weight, or even zero percent, by weight, SiO₂),         less than 20% by weight B₂O₃ (or even less than 15%, less than         10%, less than 5% by weight, or even zero percent, by weight,         B₂O₃), and less than 40% by weight P₂O₅ (or even less than 35%,         less than 30%, less than 25%, less than 20%, less than 15%, less         than 1%, less than 5% by weight, or even zero percent, by         weight, P₂O₅);     -   heating the first and second glasses above at least T_(g1) and         at least the first glass coalescing with the second glass to         provide the article. Optionally, the second glass has a T_(g2)         and T_(x2), wherein the difference between T_(g2) and T_(x2) is         at least 5K (or even, at least 10K, at least 15K, at least 20K,         at least 25K, at least 30K, or at least 35K). Optionally, the         second glass contains less than 20% by weight SiO₂ (or even less         than 15%, less than 10%, less than 5% by weight, or even zero         percent, by weight, SiO₂), less than 20% by weight B₂O₃ (or even         less than 15%, less than 10%, less than 5% by weight, or even         zero percent, by weight, B₂O₃), and less than 40% by weight P₂O₅         (or even less than 35%, less than 30%, less than 25%, less than         20%, less than 15%, less than 1%, less than 5% by weight, or         even zero percent, by weight, P₂O₅). Optionally, the method can         be practiced with a third, a fourth, glass, etc. including         glasses having, respectively, a T_(g) and T_(x), and wherein the         difference between each T_(g) and the T_(x) of a glass is at         least 5K (or even, at least 10K, at least 15K, at least 20K, at         least 25K, at least 30K, or at least 35K), one or more of the         additional glasses optionally contain less than 20% by weight         SiO₂ (or even less than 15%, less than 10%, less than 5% by         weight, or even zero percent, by weight, SiO₂), less than 20% by         weight B₂O₃ (or even less than 15%, less than 10%, less than 5%         by weight, or even zero percent, by weight, B₂O₃), and less than         40% by weight P₂O₅ (or even less than 35%, less than 30%, less         than 25%, less than 20%, less than 15%, less than 1%, less than         5% by weight, or even zero percent, by weight, P₂O₅). The         glasses may have the same composition, different composition, or         combinations thereof. Preferably at least one of the glasses         comprise less than 40 (preferably, less than 35, 30, 25, 20, 15,         10, 5, or even 0) percent by weight glass collectively SiO₂,         B₂O₃, and P₂O₅, based on the total weight of the glass.

Another embodiment of the present invention provides a method of making an article comprising:

-   -   providing at least a first glass and second glass (e.g., sheets,         particles (including microspheres), and fibers), wherein the         first glass comprises at least two different metal oxides,         wherein the first glass has a T_(g1) and T_(x1), and wherein the         difference between the T_(g1) and the T_(x1) is at least 5K (or         even, at least 10K, at least 15K, at least 20K, at least 25K, at         least 30K, or at least 35K), the first glass containing less         than 20% by weight SiO₂ (or even less than 15%, less than 10%,         less than 5% by weight, or even zero percent, by weight, SiO₂),         less than 20% by weight B₂O₃ (or even less than 15%, less than         10%, less than 5% by weight, or even zero percent, by weight,         B₂O₃), and less than 40% by weight P₂O₅ (or even less than 35%,         less than 30%, less than 25%, less than 20%, less than 15%, less         than 1%, less than 5% by weight, or even zero percent, by         weight, P₂O₅), and wherein the second glass comprises at least         two different metal oxides, wherein the second glass has a         T_(g2) and T_(x2), and wherein the difference between the T_(g2)         and the T_(x2) is at least 5K (or even, at least 10K, at least         15K, at least 20K, at least 25K, at least 30K, or at least 35K),         the second glass containing less than 20% by weight SiO₂ (or         even less than 15%, less than 10%, less than 5% by weight, or         even zero percent, by weight, SiO₂), less than 20% by weight         B₂O₃ (or even less than 15%, less than 10%, less than 5% by         weight, or even zero percent, by weight, B₂O₃), and less than         40% by weight P₂O₅ (or even less than 35%, less than 30%, less         than 25%, less than 20%, less than 15%, less than 1%, less than         5% by weight, or even zero percent, by weight, P₂O₅);     -   heating the glasses above the higher of T_(g1) or T_(g2) and         coalescing the first and second glasses to provide the article.         Optionally, the method can be practices with a third, a fourth,         glass, etc. including glasses having, respectively, a T_(g) and         T_(x), and wherein the difference between each T_(g) and the         T_(x) of a glass is at least 5K (or even, at least 10K, at least         15K, at least 20K, at least 25K, at least 30K, or at least 35K),         one or more of the additional glasses optionally contain less         than 20% by weight SiO₂ (or even less than 15%, less than 10%,         less than 5% by weight, or even zero percent, by weight, SiO₂),         less than 20% by weight B₂O₃ (or even less than 15%, less than         10%, less than 5% by weight, or even zero percent, by weight,         B₂O₃), and less than 40% by weight P₂O₅ (or even less than 35%,         less than 30%, less than 25%, less than 20%, less than 15%, less         than 1%, less than 5% by weight, or even zero percent, by         weight, P₂O₅). The glasses may have the same composition,         different composition, or combinations thereof. Preferably at         least one of the glasses comprise less than 40 (preferably, less         than 35, 30, 25, 20, 15, 10, 5, or even 0) percent by weight         glass collectively SiO₂, B₂O₃, and P₂O₅, based on the total         weight of the glass.

Another embodiment of the present invention provides a method of making an article comprising:

-   -   providing at least a first plurality of particles comprising         glass (including glass particles), wherein the glass comprises         at least two different metal oxides, wherein the glass has a         T_(g) and T_(x), and wherein the difference between the T_(g)         and the T_(x) of the glass is at least 5K (or even, at least         10K, at least 15K, at least 20K, at least 25K, at least 30K, or         at least 35K), the glass containing less than 20% by weight SiO₂         (or even less than 15%, less than 10%, less than 5% by weight,         or even zero percent, by weight, SiO₂), less than 20% by weight         B₂O₃ (or even less than 15%, less than 10%, less than 5% by         weight, or even zero percent, by weight, B₂O₃), and less than         40% by weight P₂O₅ (or even less than 35%, less than 30%, less         than 25%, less than 20%, less than 15%, less than 1%, less than         5% by weight, or even zero percent, by weight, P₂O₅);     -   heating the glass above the T_(g) and coalescing at least a         portion of the first plurality of particles to provide the         article. In some embodiments, the ceramic is glass. Optionally,         the method can be practiced with a second, a third, or more,         different pluralities of particles comprising (different)         glasses, including glasses having, respectively, a T_(g) and         T_(x), and wherein the difference between each T_(g) and the         T_(x) of a glass is at least 5K (or even, at least 10K, at least         15K, at least 20K, at least 25K, at least 30K, or at least 35K),         one or more of the additional glasses optionally contain less         than 20% by weight SiO₂ (or even less than 15%, less than 10%,         less than 5% by weight, or even zero percent, by weight, SiO₂),         less than 20% by weight B₂O₃ (or even less than 15%, less than         10%, less than 5% by weight, or even zero percent, by weight,         B₂O₃), and less than 40% by weight P₂O₅ (or even less than 35%,         less than 30%, less than 25%, less than 20%, less than 15%, less         than 1%, less than 5% by weight, or even zero percent, by         weight, P₂O₅). Preferably the glass, or if more than one glass         is used, at least one of the glasses, comprises less than 40         (preferably, less than 35, 30, 25, 20, 15, 10, 5, or even 0)         percent by weight glass collectively SiO₂, B₂O₃, and P₂O₅, based         on the total weight of the glass.

Desirably, the ratio of a T_(g) to T₁ is at least 0.5. Examples of useful glass particles include those comprising REO-Al₂O₃—ZrO₂ and REO-Al₂O₃—ZrO₂—SiO₂ glasses. Other useful glasses may also include CaO—Al₂O₃, CaO—Al₂O₃—ZrO₂, BaO—TiO₂, La₂O₃—TiO₂, REO (i.e., rare earth oxide(s))-Al₂O₃ glasses.

Embodiments of the method according to the present invention, including for certain ceramic compositions, allow for the formation of article shapes and sizes that were obtainable from conventional methods. Coalescence of the glass is typically enhanced if the glass is under pressure during heating. In one embodiment, a charge of glass (e.g., particles (including beads), fibers, etc. is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into an article.

In this application:

“amorphous material” refers to material derived from a melt and/or a vapor phase that lacks any long range crystal structure as determined by X-ray diffraction and/or has an exothermic peak corresponding to the crystallization of the amorphous material as determined by a DTA (differential thermal analysis) as determined by the test described herein entitled “Differential Thermal Analysis”;

“ceramic” includes amorphous material, glass, crystalline ceramic, glass-ceramic, and combinations thereof;

“glass” refers to amorphous material exhibiting a glass transition temperature;

“glass-ceramic” refers to ceramic comprising crystals formed by heat-treating amorphous material;

“rare earth oxides” refers to cerium oxide (e.g., CeO₂), dysprosium oxide (e.g., Dy₂O₃), erbium oxide (e.g., Er₂O₃), europium oxide (e.g., Eu₂O₃), gadolinium (e.g., Gd₂O₃), holmium oxide (e.g., Ho₂O₃), lanthanum oxide (e.g., La₂O₃), lutetium oxide (e.g., Lu₂O₃), neodymium oxide (e.g., Nd₂O₃), praseodymium oxide (e.g., Pr₆O₁₁), samarium oxide (e.g., Sm₂O₃), terbium (e.g., Tb₂O₃), thorium oxide (e.g., Th₄O₇), thulium (e.g., Tm₂O₃), and ytterbium oxide (e.g., Yb₂O₃), and combinations thereof;

“REO” refers to rare earth oxide(s);

“T_(g)” refers to the glass transition temperature as determined in Example 1;

“T₁” refers to the glass melting point; and

“T_(x)” refers to crystallization onset temperature as determined in Example 1.

Further, it is understood herein that unless it is stated that a metal oxide (e.g., Al₂O₃, complex Al₂O₃.metal oxide, etc.) is crystalline, for example, in a glass-ceramic, it may be amorphous, crystalline, or portions amorphous and portions crystalline. For example if a glass-ceramic comprises Al₂O₃ and ZrO₂, the Al₂O₃ and ZrO₂ may each be in an amorphous state, crystalline state, or portions in an amorphous state and portions in a crystalline state, or even as a reaction product with another metal oxide(s) (e.g., unless it is stated that, for example, Al₂O₃ is present as crystalline Al₂O₃ or a specific crystalline phase of Al₂O₃ (e.g., alpha Al₂O₃), it may be present as crystalline Al₂O₃ and/or as part of one or more crystalline complex Al₂O₃.metal oxides. Further, it is understood that glass-ceramics formed by heating amorphous material not exhibiting a T_(g) may not actually comprise glass, but rather may comprise the crystals and amorphous material that does not exhibiting a T_(g).

Optionally certain glass articles made according to the present invention can be heat-treated at least partially crystallize the glass to provide glass-ceramic.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a DTA curve of Example 1 material; and

FIGS. 2-6 are DTA curves of Examples 2, 5, 6, 7, and 9 materials, respectively.

DETAILED DESCRIPTION

The following disclosures are incorporated herein by reference: U.S. Ser. No. 10/211,491, filed Aug. 2, 2002; U.S. Ser. No. 09/922,526, filed Aug. 2, 2001; U.S. 2007/0135290 A1, filed Jan. 15, 2007; U.S. Ser. No. ______ (Attorney Docket No. 56938US018), filed on this same day; and U.S. Ser. No. ______ (Attorney Docket No. 56938US019), filed on this same day.

In general, ceramics according to the present invention can be made by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide amorphous materials or ceramic comprising amorphous materials. Amorphous materials and ceramics comprising amorphous materials according to the present invention can be made, for example, by heating (including in a flame) the appropriate metal oxide sources to form a melt, desirably a homogenous melt, and then rapidly cooling the melt to provide amorphous material. Embodiments of amorphous materials can be made, for example, by melting the metal oxide sources in any suitable furnace (e.g., an inductive heated furnace, a gas-fired furnace, or an electrical furnace), or, for example, in a plasma. The resulting melt is cooled (e.g., discharging the melt into a cooling media (e.g., high velocity air jets, liquids, metal plates (including chilled metal plates), metal rolls (including chilled metal rolls), metal balls (including chilled metal balls), and the like)).

Embodiments of amorphous materials can also be obtained by other techniques, such as: laser spin melt with free fall cooling, Taylor wire technique, plasmatron technique, hammer and anvil technique, centrifugal quenching, air gun splat cooling, single roller and twin roller quenching, roller-plate quenching and pendant drop melt extraction (see, e.g., Rapid Solidification of Ceramics, Brockway et. al, Metals And Ceramics Information Center, A Department of Defense Information Analysis Center, Columbus, Ohio, January, 1984, the disclosure of which is incorporated here as a reference). Embodiments of amorphous materials may also be obtained by other techniques, such as: thermal (including flame or laser or plasma-assisted) pyrolysis of suitable precursors, physical vapor synthesis (PVS) of metal precursors and mechanochemical processing.

In one method, glass useful for the present invention can be made utilizing flame fusion as disclosed, for example, in U.S. Pat. No. 6,254,981 (Castle), the disclosure of which is incorporated herein by reference. In this method, the metal oxide sources materials are fed (e.g., in the form of particles, sometimes referred to as “feed particles”) directly into a burner (e.g., a methane-air burner, an acetylene-oxygen burner, a hydrogen-oxygen burner, and like), and then quenched, for example, in water, cooling oil, air, or the like. Feed particles can be formed, for example, by grinding, agglomerating (e.g., spray-drying), melting, or sintering the metal oxide sources. The size of feed particles fed into the flame generally determines the size of the resulting glass particles/beads.

Examples of useful glass for carrying out the present invention include those comprising CaO—Al₂O₃, CaO—Al₂O₃—ZrO₂, BaO—TiO₂, La₂O₃—TiO₂, REO-Al₂O₃, REO-Al₂O₃—ZrO₂, REO-Al₂O₃—ZrO₂—SiO₂, and SrO—Al₂O₃—ZrO₂ glasses. Useful glass formulations include those at or near a eutectic composition. In addition to the CaO—Al₂O₃, CaO—Al₂O₃—ZrO₂, BaO—TiO₂, La₂O₃—TiO₂, REO-Al₂O₃, REO-Al₂O₃—ZrO₂, REO-Al₂O₃—ZrO₂—SiO₂, and SrO—Al₂O₃—ZrO₂ compositions disclosed herein, other compositions, including eutectic compositions, will be apparent to those skilled in the art after reviewing the present disclosure. For example, phase diagrams depicting various compositions, including eutectic compositions, are known in the art.

Surprisingly, it was found that ceramics of present invention could be obtained without limitations in dimensions. This was found to be possible through a coalescence step performed at temperatures above glass transition temperature. For instance, as evident from FIG. 1, glass useful in carry out the present invention undergoes glass transition (T_(g)) before significant crystallization occurs (T_(x)) as evidenced by the existence of endotherm (T_(g)) at lower temperature than exotherm (T_(x)). This allows for bulk fabrication of articles of any dimensions from relatively small pieces of glass. More specifically, for example, an article according to the present invention, can be provided by heating, for example, glass particles (including beads and microspheres), fibers, etc. useful in carrying out the present invention above the T_(g) such that the glass particles, etc. coalesce to form a shape and cooling the coalesced shape to provide the article. In certain embodiments, heating is conducted at least one temperature in a range of about 725° C. to about 1100° C.

Surprisingly, for certain embodiments according to the present invention, coalescence may be conducted at temperatures significantly higher than crystallization temperature (T_(x)). Although not wanting to be bound by theory, it s is believed the relatively slow kinetics of crystallization allow access to higher temperatures for viscous flow. Typically, the glass is under pressure during coalescence to aid the coalescence of the glass. In one embodiment, a charge of the glass particles, etc. is placed into a die and hot-pressing is performed at temperatures above glass transition where viscous flow of glass leads to coalescence into a relatively large part. Typically, the amorphous material is under pressure (e.g., greater than zero to 1 GPa or more) during coalescence to aid the coalescence of the amorphous material. It is also within the scope of the present invention to conduct additional coalescence to further improve desirable properties of the article. For example, hot-isostatic pressing may be conducted (e.g., at temperatures from about 900° C. to about 1400° C.) to remove residual porosity, increasing the density of the material. It is also within the scope of the present invention to coalesce glass via hot-isostatic pressing, hot extrusion, or other pressure assisted techniques.

Heat-treatment can be carried out in any of a variety of ways, including those known in the art for heat-treating glass to provide glass-ceramics. For example, heat-treatment can be conducted in batches, for example, using resistive, inductively or gas heated furnaces. Alternatively, for example, heat-treatment can be conducted continuously, for example, using rotary kilns. In the case of a rotary kiln, the material is fed directly into a kiln operating at the elevated temperature. The time at the elevated temperature may range from a few seconds (in some embodiments even less than 5 seconds) to a few minutes to several hours. The temperature may range anywhere from 900° C. to 1600° C., typically between 1200° C. to 1500° C. It is also within the scope of the present invention to perform some of the heat-treatment in batches (e.g., for the nucleation step) and another continuously (e.g., for the crystal growth step and to achieve the desired density). For the nucleation step, the temperature typically ranges between about 900° C. to about 1100° C., in some embodiments, preferably in a range from about 925° C. to about 1050° C. Likewise for the density step, the temperature typically is in a range from about 1100° C. to about 1600° C., in some embodiments, preferably in a range from about 1200° C. to about 1500° C. This heat treatment may occur, for example, by feeding the material directly into a furnace at the elevated temperature. Alternatively, for example, the material may be feed into a furnace at a much lower temperature (e.g., room temperature) and then heated to desired temperature at a predetermined heating rate. It is within the scope of the present invention to conduct heat-treatment in an atmosphere other than air. In some cases it might be even desirable to heat-treat in a reducing atmosphere(s). Also, for, example, it may be desirable to heat-treat under gas pressure as in, for example, hot-isostatic press, or in gas pressure furnace.

Sources, including commercial sources, of metal oxides such as Al₂O₃, BaO, CaO, rare earth oxides (e.g., CeO₂, Dy₂O₃, Er₂O₃, Eu₂O₃, Gd₂O₃, Ho₂O₃, La₂O₃, Lu₂O₃, Nd₂O₃, Pr₆O₁₁, Sm₂O₃, Th₄O₇, Tm₂O₃, and Yb₂O₃, and combinations thereof), TiO₂, ZrO₂ are known in the art. For example sources of (on a theoretical oxide basis) Al₂O₃ include bauxite (including both natural occurring bauxite and synthetically produced bauxite), calcined bauxite, hydrated aluminas (e.g., boehmite, and gibbsite), aluminum, Bayer process alumina, aluminum ore, gamma alumina, alpha alumina, aluminum salts, aluminum nitrates, and combinations thereof. The Al₂O₃ source may contain, or only provide, Al₂O₃. Alternatively, the Al₂O₃ source may contain, or provide Al₂O₃, as well as one or more metal oxides other than Al₂O₃ (including materials of or containing complex Al₂O₃ metal oxides (e.g., Dy₃Al₅O₁₂, Y₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of rare earth oxides include rare earth oxide powders, rare earth metals, rare earth-containing ores (e.g., bastnasite and monazite), rare earth salts, rare earth nitrates, and rare earth carbonates. The rare earth oxide(s) source may contain, or only provide, rare earth oxide(s). Alternatively, the rare earth oxide(s) source may contain, or provide rare earth oxide(s), as well as one or more metal oxides other than rare earth oxide(s) (including materials of or containing complex rare earth oxide.other metal oxides (e.g., Dy₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO₂ include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO₂ source may contain, or provide ZrO₂, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO₂ include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO₂ source may contain, or provide HfO₂, as well as other metal oxides such as ZrO₂.

Sources, including commercial sources, of BaO include barium oxide powders, barium-containing ores, barium salts, barium nitrates, and barium carbonates. The barium oxide source may contain, or only provide, barium oxide. Alternatively, the barium oxide source may contain, or provide barium oxide, as well as one or more metal oxides other than barium oxide (including materials of or containing complex barium oxide).

Sources, including commercial sources, of CaO include calcium oxide powders and calcium-containing ores. The calcium oxide(s) source may contain, or only provide, calcium oxide. Alternatively, the calcium oxide source may contain, or provide calcium oxide, as well as one or more metal oxides other than calcium oxide (including materials of or containing complex calcium oxide).

Sources, including commercial sources, of rare earth oxides include rare earth oxide powders, rare earth metals, rare earth-containing ores (e.g., bastnasite and monazite), rare earth salts, rare earth nitrates, and rare earth carbonates. The rare earth oxide(s) source may contain, or only provide, rare earth oxide(s). Alternatively, the rare earth oxide(s) source may contain, or provide rare earth oxide(s), as well as one or more metal oxides other than rare earth oxide(s) (including materials of or containing complex rare earth oxides (e.g., Dy₃Al₅O₁₂, CeAl₁₁O₁₈, etc.)).

Sources, including commercial sources, of SiO₂ include silica powders, silicon metals, silicon-containing ores. The silicon oxide source may contain, or only provide, silicon oxide. Alternatively, the silicon oxide source may contain, or provide silicon oxide, as well as one or more metal oxides other than silicon oxide (including materials of or containing complex silicon oxide other metal oxides).

Sources, including commercial sources, of SrO include strontium oxide powders, strontium carbonates, and strontium-containing ores. The strontium oxide source may contain, or only provide, strontium oxide. Alternatively, the strontium oxide source may contain, or provide strontium oxide, as well as one or more metal oxides other than strontium oxide (including materials of or containing complex strontium oxide).

Sources, including commercial sources, of TiO₂ include titanium oxide powders, titanium metals and titanium-containing ores. The titanium oxide source may contain, or only provide, titanium oxide. Alternatively, the titanium oxide source may contain, or provide titanium oxide, as well as one or more metal oxides other than titanium oxide (including materials of or containing complex titanium oxide).

Sources, including commercial sources, of (on a theoretical oxide basis) ZrO₂ include zirconium oxide powders, zircon sand, zirconium, zirconium-containing ores, and zirconium salts (e.g., zirconium carbonates, acetates, nitrates, chlorides, hydroxides, and combinations thereof). In addition, or alternatively, the ZrO₂ source may contain, or provide ZrO₂, as well as other metal oxides such as hafnia. Sources, including commercial sources, of (on a theoretical oxide basis) HfO₂ include hafnium oxide powders, hafnium, hafnium-containing ores, and hafnium salts. In addition, or alternatively, the HfO₂ source may contain, or provide HfO₂, as well as other metal oxides such as ZrO₂.

Optionally, ceramics according to the present invention further comprise additional metal oxides beyond those needed for the general composition. The addition of certain metal oxides may alter the properties and/or the crystalline structure or microstructure of ceramics made according to the present invention, as well as the processing of the raw materials and intermediates in making the ceramic. For example, oxide additions such as MgO, CaO, Li₂O, and Na₂O have been observed to alter both the T_(g) and T_(x) of glass. Although not wishing to be bound by theory, it is believed that such additions influence glass formation. Further, for example, such oxide additions may decrease the melting temperature of the overall system (i.e., drive the system toward lower melting eutectic), and ease of glass-formation. Complex eutectics in multi component systems (quaternary, etc.) may result in better glass-forming ability. The viscosity of the liquid melt and viscosity of the glass in its' “working” range may also be affected by the addition of metal oxides beyond those needed for the general composition.

In some instances, it may be preferred to incorporate limited amounts of metal oxides selected from the group consisting of: Na₂O, P₂O₅, SiO₂, TeO₂, V₂O₃, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. These metal oxides may be added, for example, to modify a physical property of the resulting abrasive particles and/or improve processing. These metal oxides when used are typically are added from greater than 0 to 20% by weight, preferably greater than 0 to 5% by weight and more preferably greater than 0 to 2% by weight of the glass-ceramic depending, for example, upon the desired property.

Further other glass compositions which may be used in conjunction with the required glass(es) for carrying out the present invention include those conventional glasses that are well known in the art, including sources thereof.

For glasses that devitrify to form glass-ceramics, crystallization may also be affected by the additions of materials beyond those needed for the general composition. For example, certain metals, metal oxides (e.g., titanates and zirconates), and fluorides, for example, may act as nucleation agents resulting in beneficial heterogeneous nucleation of crystals. Also, addition of some oxides may change nature of metastable phases devitrifying from the glass upon reheating. In another aspect, for ceramics according to the present invention comprising crystalline ZrO₂, it may be desirable to add metal oxides (e.g., Y₂O₃, TiO₂, CaO, and MgO) that are known to stabilize tetragonal/cubic form of ZrO₂.

Examples of optional metal oxides (i.e., metal oxides beyond those needed for the general composition) may include, on a theoretical oxide basis, Al₂O₃, BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, HfO₂, Li₂O, MgO, MnO, NiO, Na₂O, P₂O₅, rare earth oxides, Sc₂O₃, SiO₂, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, ZrO₂, and combinations thereof. Sources, including commercial sources, include the oxides themselves, complex oxides, ores, carbonates, acetates, nitrates, chlorides, hydroxides, etc. Further, for example, with regard to Y₂O₃, sources, including commercial sources, of (on a theoretical oxide basis) Y₂O₃ include yttrium oxide powders, yttrium, yttrium-containing ores, and yttrium salts (e.g., yttrium carbonates, nitrates, chlorides, hydroxides, and combinations thereof). The Y₂O₃ source may contain, or only provide, Y₂O₃. Alternatively, the Y₂O₃ source may contain, or provide Y₂O₃, as well as one or more metal oxides other than Y₂O₃ (including materials of or containing complex Y₂O₃ (e.g., Y₃Al₅O₁₂)).

In some embodiments, it may be advantageous for at least a portion of a metal oxide source (in some embodiments, preferably, 10 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or even at least 95 percent by weight) to be obtained by adding particulate, metallic material comprising at least one of a metal (e.g., Al, Ca, Cu, Cr, Fe, Li, Mg, Ni, Ag, Ti, Zr, and combinations thereof), M, that has a negative enthalpy of oxide formation or an alloy thereof to the melt, or otherwise metal them with the other raw materials. Although not wanting to be bound by theory, it is believed that the heat resulting from the exothermic reaction associated with the oxidation of the metal is beneficial in the formation of a homogeneous melt and resulting amorphous material. For example, it is believed that the additional heat generated by the oxidation reaction within the raw material eliminates or minimizes insufficient heat transfer, and hence facilitates formation and homogeneity of the melt, particularly when forming amorphous particles with x, y, and z dimensions over 150 micrometers. It is also believed that the availability of the additional heat aids in driving various chemical reactions and physical processes (e.g., densification, and spherodization) to completion. Further, it is believed for some embodiments, the presence of the additional heat generated by the oxidation reaction actually enables the formation of a melt, which otherwise is difficult or otherwise not practical due to high melting point of the materials. Further, the presence of the additional heat generated by the oxidation reaction actually enables the formation of amorphous material that otherwise could not be made, or could not be made in the desired size range. Another advantage of the invention include, in forming the amorphous materials, that many of the chemical and physical processes such as melting, densification and spherodizing can be achieved in a short time, so that very high quench rates be can achieved. For additional details, see U.S. Pat. No. 7,168,267 (Rosenflanz et al.), the disclosure of which is incorporated herein by reference.

The particular selection of metal oxide sources and other additives for making ceramics according to the present invention typically takes into account, for example, the desired composition and microstructure of the resulting ceramics, the desired degree of crystallinity, if any, the desired physical properties (e.g., hardness or toughness) of the resulting ceramics, avoiding or minimizing the presence of undesirable impurities, the desired characteristics of the resulting ceramics, and/or the particular process (including equipment and any purification of the raw materials before and/or during fusion and/or solidification) being used to prepare the ceramics.

The metal oxide sources and other additives can be in any form suitable to the process and equipment utilized for the present invention. The raw materials can be melted and quenched using techniques and equipment known in the art for making oxide glasses and amorphous metals. Desirable cooling rates include those of 50K/s and greater. Cooling techniques known in the art include roll-chilling. Roll-chilling can be carried out, for example, by melting the metal oxide sources at a temperature typically 20-200° C. higher than the melting point, and cooling/quenching the melt by spraying it under high pressure (e.g., using a gas such as air, argon, nitrogen or the like) onto a high-speed rotary roll(s). Typically, the rolls are made of metal and are water cooled. Metal book molds may also be useful for cooling/quenching the melt.

Other techniques for forming melts, cooling/quenching melts, and/or otherwise forming glass include vapor phase quenching, plasma spraying, melt-extraction, and gas atomization. Vapor phase quenching can be carried out, for example, by sputtering, wherein the metal alloys or metal oxide sources are formed into a sputtering target(s) which are used. The target is fixed at a predetermined position in a sputtering apparatus, and a substrate(s) to be coated is placed at a position opposing the target(s). Typical pressures of 10⁻³ torr of oxygen gas and Ar gas, discharge is generated between the target(s) and a substrate(s), and Ar or oxygen ions collide against the target to start reaction sputtering, thereby depositing a film of composition on the substrate. For additional details regarding plasma spraying, see, for example, U.S. Pat. No. 7,179,526 (Rosenflanz et al.), the disclosure of which is incorporated herein by reference.

Gas atomization involves melting feed particles to convert them to melt. A thin stream of such melt is atomized through contact with a disruptive air jet (i.e., the stream is divided into fine droplets). The resulting substantially discrete, generally ellipsoidal glass particles are then recovered. Melt-extraction can be carried out, for example, as disclosed in U.S. Pat. No. 5,605,870 (Strom-Olsen et al.), the disclosure of which is incorporated herein by reference. Containerless glass forming techniques utilizing laser beam heating as disclosed, for example, in PCT application having Publication No. WO 01/27046 A1, published Apr. 4, 2001, the disclosure of which is incorporated herein by reference, may also be useful in making glass according to the present invention.

The cooling rate is believed to affect the properties of the quenched amorphous material. For instance, glass transition temperature, density and other properties of glass typically change with cooling rates.

Rapid cooling may also be conducted under controlled atmospheres, such as a reducing, neutral, or oxidizing environment to maintain and/or influence the desired oxidation states, etc. during cooling. The atmosphere can also influence glass formation by influencing crystallization kinetics from undercooled liquid. For example, larger undercooling of Al₂O₃ melts without crystallization has been reported in argon atmosphere as compared to that in air.

With regard to making particles, for example, the resulting ceramic (e.g., glass or ceramic comprising glass may be larger in size than that desired. The ceramic can be, and typically is, converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. In some instances, it is desired to have two or multiple crushing steps. For example, after the ceramic is formed (solidified), it may be in the form larger than desired. The first crushing step may involve crushing these relatively large masses or “chunks” to form smaller pieces. This crushing of these chunks may be accomplished with a hammer mill, impact crusher or jaw crusher. These smaller pieces may then be subsequently crushed to produce the desired particle size distribution. In order to produce the desired particle size distribution (sometimes referred to as grit size or grade), it may be necessary to perform multiple crushing steps. In general the crushing conditions are optimized to achieve the desired particle shape(s) and particle size distribution.

The shape of particles can depend, for example, on the composition of the glass, the geometry in which it was cooled, and the manner in which the glass is crushed (i.e., the crushing technique used), if the particles were formed by crushing.

Certain articles according to the present invention comprising glass can be heat-treated to increase or at least partially crystallize the glass (including crystallize the glass) to provide glass-ceramic. The heat-treatment of certain glasses to form glass-ceramics is well known in the art. The heating conditions to nucleate and grow glass-ceramics are known for a variety of glasses. Alternatively, one skilled in the art can determine the appropriate conditions from a Time-Temperature-Transformation (TTT) study of the glass using techniques known in the art. One skilled in the art, after reading the disclosure of the present invention should be able to provide TTT curves for glasses according to the present invention, determine the appropriate nucleation and/or crystal growth conditions to provide crystalline ceramics, glass-ceramics, and ceramic comprising glass according to the present invention.

Typically, glass-ceramics are stronger than the glasses from which they are formed. Hence, the strength of the material may be adjusted, for example, by the degree to which the glass is converted to crystalline ceramic phase(s). Alternatively, or in addition, the strength of the material may also be affected, for example, by the number of nucleation sites created, which may in turn be used to affect the number, and in turn the size of the crystals of the crystalline phase(s). For additional details regarding forming glass-ceramics, see, for example Glass-Ceramics, P. W. McMillan, Academic Press, Inc., 2^(nd) edition, 1979, the disclosure of which is incorporated herein by reference.

For example, during heat-treatment of a glass such as a glass comprising Al₂O₃, La₂O₃, and ZrO₂ formation of phases such as La₂Zr₂O₇, and, if ZrO₂ is present, cubic/tetragonal ZrO₂, in some cases monoclinic ZrO₂, have been observed at temperatures above about 900° C. Although not wanting to be bound by theory, it is believed that zirconia-related phases are the first phases to nucleate from the glass. For example, of Al₂O₃, ReAlO₃ (wherein Re is at least one rare earth cation), ReAl₁₁O₁₈, Re₃Al₅O₁₂, Y₃Al₅O₁₂, etc. phases are believed to generally occur at temperatures above about 925° C. Crystallite size during this nucleation step may be on the order of nanometers. For example, crystals as small as 10-15 nanometers have been observed. Longer heat-treating temperatures typically lead to the growth of crystallites and progression of crystallization. For at least some embodiments, heat-treatment at about 1300° C. for about 1 hour provides a full crystallization.

Certain ceramic articles made according to the present invention contain less than less than 20% by weight SiO₂ (or even less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, SiO₂), less than 20% by weight B₂O₃ (or even less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, B₂O₃), and less than 40% by weight P₂O₅ (or even less than 35%, less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than, 5% by weight, or even zero percent, by weight, P₂O₅), based on the total metal oxide weight of the ceramic.

The microstructure or phase composition (glassy/amorphous/crystalline) of a material can be determined in a number of ways. Various information can be obtained using optical microscopy, electron microscopy, differential thermal analysis (DTA), and x-ray diffraction (XRD), for example.

Using optical microscopy, amorphous material is typically predominantly transparent due to the lack of light scattering centers such as crystal boundaries, while crystalline material shows a crystalline structure and is opaque due to light scattering effects.

Using DTA, the material is classified as amorphous if the corresponding DTA trace of the material contains an exothermic crystallization event (T_(x)). If the same trace also contains an endothermic event (T_(g)) at a temperature lower than T_(x) it is considered to consist of a glass phase. If the DTA trace of the material contains no such events, it is considered to contain crystalline phases.

Differential thermal analysis (DTA) can be conducted using the following method. DTA runs can be made (using an instrument such as that obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”) using a −140+170 mesh size fraction (i.e., the fraction collected between 105-micrometer opening size and 90-micrometer opening size screens). An amount of each screened sample (typically about 400 milligrams (mg)) is placed in a 100-microliter Al₂O₃ sample holder. Each sample is heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1100° C.

Using powder x-ray diffraction, XRD, (using an x-ray diffractometer such as that obtained under the trade designation “PHILLIPS XRG 3100” from Phillips, Mahwah, N.J., with copper Kα1 radiation of 1.54050 Angstrom) the phases present in a material can be determined by comparing the peaks present in the XRD trace of the crystallized material to XRD patterns of crystalline phases provided in JCPDS (Joint Committee on Powder Diffraction Standards) databases, published by International Center for Diffraction Data. Furthermore, an XRD can be used qualitatively to determine types of phases. The presence of a broad diffused intensity peak is taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks is taken as an indication of existence of crystalline matter within an amorphous matrix. The initially formed amorphous material or ceramic (including glass prior to crystallization) may be larger in size than that desired. The amorphous material or ceramic can be converted into smaller pieces using crushing and/or comminuting techniques known in the art, including roll crushing, canary milling, jaw crushing, hammer milling, ball milling, jet milling, impact crushing, and the like. In some instances, it is desired to have two or multiple crushing steps. For example, after the ceramic is formed (solidified), it may be in the form of larger than desired. The first crushing step may involve crushing these relatively large masses or “chunks” to form smaller pieces. This crushing of these chunks may be accomplished with a hammer mill, impact crusher or jaw crusher. These smaller pieces may then be subsequently crushed to produce the desired particle size distribution. In order to produce the desired particle size distribution (sometimes referred to as grit size or grade), it may be necessary to perform multiple crushing steps. In general the crushing conditions are optimized to achieve the desired particle shape(s) and particle size distribution. Resulting particles that are of the desired size may be recrushed if they are too large, or “recycled” and used as a raw material for re-melting if they are too small.

The shape of particles can depend, for example, on the composition and/or microstructure of the ceramic, the geometry in which it was cooled, and the manner in which the ceramic is crushed (i.e., the crushing technique used). In general, where a “blocky” shape is preferred, more energy may be employed to achieve this shape. Conversely, where a “sharp” shape is preferred, less energy may be employed to achieve this shape. The crushing technique may also be changed to achieve different desired shapes. For some particles an average aspect ratio ranging from 1:1 to 5:1 is typically desired, and in some embodiments 1.25:1 to 3:1, or even 1.5:1 to 2.5:1.

Ceramic articles (including glass-ceramics) made according to the present invention may comprise at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 1 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.5 micrometer. In another aspect, ceramics (including glass-ceramics) according to the present invention comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.3 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may comprise less than at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystallites, wherein the crystallites have an average size of less than 0.15 micrometer. In another aspect, ceramic articles (including glass-ceramics) made according to the present invention may be free of at least one of eutectic microstructure features (i.e., is free of colonies and lamellar structure) or a non-cellular microstructure.

In another aspect, certain ceramic articles made according to the present invention may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or even 100 percent by volume glass. In another aspect, certain ceramic articles made according to the present invention may comprise, for example, 100 or at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic.

Certain articles made according to the present invention comprise glass comprising CaO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the CaO and Al₂O₃, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising CaO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the CaO and Al₂O₃, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising CaO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises CaO and Al₂O₃, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the CaO and Al₂O₃, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising CaO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises CaO and Al₂O₃, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Certain articles made according to the present invention comprise glass comprising CaO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the CaO, Al₂O₃, and ZrO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising CaO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the CaO and Al₂O₃, and ZrO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising CaO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the CaO, Al₂O₃, and ZrO₂, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the CaO, Al₂O₃, and ZrO₂, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising CaO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises CaO, Al₂O₃, and ZrO₂, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Certain articles made according to the present invention comprise glass comprising BaO and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the BaO and TiO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising BaO and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the BaO and TiO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising BaO and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the BaO and TiO₂, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the BaO and TiO₂, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising BaO and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises BaO and TiO₂, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Certain articles made according to the present invention comprise glass comprising La₂O₃ and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the La₂O₃ and TiO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising La₂O₃ and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the La₂O₃ and TiO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising La₂O₃ and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the La₂O₃ and TiO₂, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 1, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the La₂O₃ and TiO₂, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising La₂O₃ and TiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises La₂O₃ and TiO₂, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Certain articles made according to the present invention comprise glass comprising REO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al₂O₃, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising REO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al₂O₃, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising REO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the REO and Al₂O₃, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, the present invention provides glass-ceramic comprising REO and Al₂O₃, wherein, for example, glass-ceramic exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300, 200, or 150 nanometers; and in some embodiments, less than 100, 75, 50, 25, or 20 nanometers), and (b) is free of at least one of eutectic microstructure features or a non-cellular microstructure. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the REO and Al₂O₃, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising REO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises REO and Al₂O₃, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Certain articles made according to the present invention comprise glass comprising REO and Al₂O₃, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al₂O₃, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising REO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al₂O₃ and ZrO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising REO, Al₂O₃, and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the REO and Al₂O₃ and ZrO₂, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, the present invention provides glass-ceramic comprising REO, Al₂O₃, and ZrO₂, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300, 200, or 150 nanometers; and in some embodiments, less than 100, 75, 50, 25, or 20 nanometers), and (b) is free of at least one of eutectic microstructure features or a non-cellular microstructure. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the REO, Al₂O₃, and ZrO₂, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising REO and Al₂O₃ and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises REO, Al₂O₃, and ZrO₂, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising glass (e.g., at least 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume glass), the glass comprising REO, Al₂O₃, ZrO₂, and SiO₂ wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass collectively comprises the REO and Al₂O₃ and ZrO₂, based on the total weight of the glass.

In another aspect, certain articles made according to the present invention provides glass-ceramic comprising REO, Al₂O₃, ZrO₂, and SiO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the glass-ceramic collectively comprises the REO and Al₂O₃ and ZrO₂, based on the total weight of the glass-ceramic. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, or 95 percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, the present invention provides glass-ceramic comprising REO, Al₂O₃, ZrO₂, and SiO₂, wherein the glass-ceramic (a) exhibits a microstructure comprising crystallites having an average crystallite size of less than 1 micrometer (typically, less than 500 nanometers, even less than 300, 200, or 150 nanometers; and in some embodiments, less than 100, 75, 50, 25, or 20 nanometers), and (b) is free of at least one of eutectic microstructure features or a non-cellular microstructure. The glass-ceramic may comprise, for example, at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, percent by volume glass. The glass-ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, or 5 percent by volume crystalline ceramic.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the crystalline ceramic comprising, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the crystalline ceramic collectively comprises the REO, Al₂O₃, ZrO₂, and SiO₂, based on the total weight of the crystalline ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

In another aspect, certain articles made according to the present invention provides a ceramic comprising crystalline ceramic (e.g., at least 1, 2, 3, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 97, 98, 99, or even 100 percent by volume crystalline ceramic), the ceramic comprising REO and Al₂O₃ and ZrO₂, wherein at least 80 (85, 90, 95, 97, 98, 99, or even 100) percent by weight of the ceramic collectively comprises REO, Al₂O₃, ZrO₂, and SiO₂, based on the total weight of the ceramic. The ceramic may comprise, for example, at least 99, 98, 97, 95, 90, 85, 80, 75, 70, 65, 60, 55, 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 3, 2, or 1 percent by volume glass.

Crystalline phases that may be present in ceramics according to the present invention include alumina (e.g., alpha and transition aluminas), BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, HfO₂, Li₂O, MgO, MnO, NiO, Na₂O, P₂O₅, REO, Sc₂O₃, SiO₂, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, ZrO₂, “complex metal oxides” (including “complex Al₂O₃-metal oxide (e.g., complex Al₂O₃-REO)), and combinations thereof.

Additional details regarding ceramics comprising Al₂O₃, at least one of REO or Y₂O₃, and at least one of ZrO₂ or HfO₂, including making, using, and properties, can be found in application having U.S. Ser. Nos. 09/922,527, 09/922,528, and 09/922,530, filed Aug. 2, 2001; U.S. 2003/0115805 A1 (Rosenflanz et al.); U.S. 2003/0110707 A1 (Rosenflanz et al.); U.S. Pat. No. 7,168,267 (Rosenflanz et al.); U.S. 2003/0126802 A1 (Rosenflanz); U.S. Pat. No. 7,147,544 (Rosenflanz et al.); and U.S. Pat. No. 7,101,819 (Rosenflanz et al., the disclosures of which are incorporated herein by reference.

Typically, and desirably, the (true) density, sometimes referred to as specific gravity, of ceramic according to the present invention is typically at least 70% of theoretical density. More desirably, the (true) density of ceramic according to the present invention is at least 75%, 80%, 85%, 90%, 95%, 96%, 97%, 98%, 99%, 99.5% or 100% of theoretical density.

Examples of articles according of the present invention include kitchenware (e.g., plates), dental brackets, and reinforcing fibers, cutting tool inserts, abrasive materials, and structural components of gas engines, (e.g., valves and bearings). Other articles include those having a protective coating of ceramic on the outer surface of a body or other substrate. Further, for example, ceramic according to the present invention can be used as a matrix material. For example, ceramics according to the present invention can be used as a binder for ceramic materials and the like such as diamond, cubic-BN, Al₂O₃, ZrO₂, Si₃N₄, and SiC. Examples of useful articles comprising such materials include composite substrate coatings, cutting tool inserts abrasive agglomerates, and bonded abrasive articles such as vitrified wheels. The use of ceramics according to the present invention can be used as binders may, for example, increase the modulus, heat resistance, wear resistance, and/or strength of the composite article.

Advantages and embodiments of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. All parts and percentages are by weight unless otherwise indicated. Unless otherwise stated, all examples contained no significant amount of SiO₂, B₂O₃, P₂O₅, GeO₂, TeO₂, As₂O₃, and V₂O₅.

EXAMPLES Example 1

A polyethylene bottle was charged with 27.5 grams of alumina particles (obtained under the trade designation “APA-0.5” from Condea Vista, Tucson, Ariz.), 22.5 grams of calcium oxide particles (obtained from Alfa Aesar, Ward Hill, Mass.) and 90 grams of isopropyl alcohol. About 200 grams of zirconia milling media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”) were added to the bottle, and the mixture was milled at 120 revolutions per minute (rpm) for 24 hours. After the milling, the milling media were removed and the slurry was poured onto a glass (“PYREX”) pan where it was dried using a heat-gun. The dried mixture was ground with a mortar and pestle and screened through a 70-mesh screen (212-micrometer opening size).

After grinding and screening, some of the particles were fed into a hydrogen/oxygen torch flame. The torch used to melt the particles, thereby generating melted glass beads, was a Bethlehem bench burner PM2D model B, obtained from Bethlehem Apparatus Co., Hellertown, Pa., delivering hydrogen and oxygen at the following rates. For the inner ring, the hydrogen flow rate was 8 standard liters per minute (SLPM) and the oxygen flow rate was 3 SLPM. For the outer ring, the hydrogen flow rate was 23 (SLPM) and the oxygen flow rate was 9.8 SLPM. The dried and sized particles were fed directly into the torch flame, where they were melted and transported to an inclined stainless steel surface (approximately 51 centimeters (cm) (20 inches) wide with the slope angle of 45 degrees) with cold water running over (approximately 8 liters/minute) the surface to form beads.

Examples 2-9

Examples 2-9 glass beads were prepared as described in Example 1, except the raw materials and the amounts of raw materials used are listed in Table 1, below, and the milling of the raw materials was carried out in 90 (milliliters) ml of isopropyl alcohol with 200 grams of the zirconia media (obtained from Tosoh Ceramics, Division of Bound Brook, N.J., under the trade designation “YTZ”) at 120 rpm for 24 hours. The sources of the raw materials used are listed in Table 2, below.

TABLE 1 Weight percent Batch Example of components amounts, g 2 CaO: 36 CaO: 18 Al₂O₃: 44 Al₂O₃: 22 ZrO₂: 20 ZrO₂: 10 3 La₂O₃: 45 La₂O₃: 22.5 TiO₂: 55 TiO₂: 27.5 4 La₂O₃: 36 La₂O₃: 18 TiO₂: 44 TiO₂: 22 ZrO₂: 20 ZrO₂: 10 5 BaO: 47.5 BaO: 23.75 TiO₂: 52.5 TiO₂: 26.25 6 La₂O₃: 48 La₂O₃: 24 Al₂O₃: 52 Al₂O₃: 26 7 La₂O₃: 40.9 La₂O₃: 20.45 Al₂O₃: 40.98 Al₂O₃: 20.49 ZrO₂: 18.12 ZrO₂: 9.06 8 La₂O₃: 43 La₂O₃: 21.5 Al₂O₃: 32 Al₂O₃: 16 ZrO₂: 12 ZrO₂: 6 SiO₂: 13 SiO₂: 6.5 9 SrO: 22.95 SrO: 11.47 Al₂O₃: 62.05 Al₂O₃: 31.25 ZrO₂: 15 ZrO₂: 7.5

TABLE 2 Raw Material Source Alumina particles (Al₂O₃) Obtained from Condea Vista, Tucson, AZ under the trade designation “APA-0.5” Calcium oxide particles (CaO) Obtained from Alfa Aesar, Ward Hill, MA Lanthanum oxide particles Obtained from Molycorp Inc., Mountain (La₂O₃) Pass, CA Silica particles (SiO₂) Obtained from Alfa Aesar Barium oxide particles (BaO) Obtained from Aldrich Chemical Co. Titanium dioxide particles Obtained from Kemira Inc., Savannah, (TiO₂) GA Strontium oxide particles Obtained from Alfa Aesar (SrO) Yttria-stabilized zirconium Obtained from Zirconia Sales, Inc. of oxide particles (Y-PSZ) Marietta, GA under the trade designation “HSY-3”

Various properties/characteristics of some of Examples 1-9 materials were measured as follows. Powder X-ray diffraction (using an X-ray diffractometer (obtained under the trade designation “PHILLIPS XRG 3100” from PHILLIPS, Mahwah, N.J.) with copper K <1 radiation of 1.54050 Angstrom)) was used to qualitatively measure phases present in example materials. The presence of a broad diffused intensity peak was taken as an indication of the amorphous nature of a material. The existence of both a broad peak and well-defined peaks was taken as an indication of existence of crystalline matter within an amorphous matrix. Phases detected in various examples are reported in Table 3, below.

TABLE 3 Phases detected via Hot-pressing Example X-ray diffraction Color T_(g), ° C. T_(x), ° C. temp, ° C. 1 Amorphous* Clear 850 987 985 2 Amorphous* Clear 851 977 975 3 Amorphous* Clear 799 875 880 4 Amorphous* Clear 821 876 880 5 Amorphous* Clear 724 760 815 6 Amorphous* Clear 855 920 970 7 Amorphous* Clear 839 932 965 8 Amorphous* Clear 836 1002 970 9 Amorphous* Clear 875 934 975 *glass, as the example has a T_(g)

For differential thermal analysis (DTA), a material was screened to retain glass beads within the 90-125 micrometer size range. DTA runs were made (using an instrument obtained from Netzsch Instruments, Selb, Germany under the trade designation “NETZSCH STA 409 DTA/TGA”). The amount of each screened sample placed in a 100-microliter Al₂O₃ sample holder was 400 milligrams. Each sample was heated in static air at a rate of 10° C./minute from room temperature (about 25° C.) to 1200° C.

Referring to FIG. 1, line 375 is the plotted DTA data for the Example 1 material. Referring to FIG. 1 line 375, the material exhibited an endothermic event at a temperature around 799° C., as evidenced by the downward curve of line 375. It was believed that this event was due to the glass transition (T_(g)) of the material. At about 875° C., an exothermic event was observed as evidenced by the sharp peak in line 345. It was believed that this event was due to the crystallization (T_(x)) of the material. These T_(g) and T_(x) values for other examples are reported in Table 3, above.

FIGS. 2-6 are the plotted DTA data for Examples 2, 5, 6, 7, and 9, respectively.

For each of Examples 1-9, about 25 grams of the glass beads were placed in a graphite die and hot-pressed using uniaxial pressing apparatus (obtained under the trade designation “HP-50”, Thermal Technology Inc., Brea, Calif.). The hot-pressing was carried out in an argon atmosphere and 13.8 megapascals (MPa) (2000 pounds per square inch (2 ksi)) pressure. The hot-pressing temperature at which appreciable glass flow occurred, as indicated by the displacement control unit of the hot pressing equipment described above, are reported for Examples 1-9 in Table 3, above.

Various modifications and alterations of this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention, and it should be understood that this invention is not to be unduly limited to the illustrative embodiments set forth herein. 

1. A method of making an article, comprising: providing a glass in a form comprising particles, beads, microspheres, or fibers; the glass comprising: REO-Al₂O₃; 0 to less than 20% by weight SiO₂; 0 to less than 20% by weight B₂O₃; and 0 to less than 40% by weight P₂O₅; the glass having a glass transition temperature, T_(g), and a crystallization onset temperature, T_(x), and the difference between T_(g) and T_(x) is at least 25K; heating the glass above the T_(g) such that the particles, beads, microspheres, or fibers coalesce to form a coalesced shape; and cooling the coalesced shape to form the article.
 2. The method of claim 1, the glass further comprising an additional metal oxide selected from the group consisting of BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, HfO₂, Li₂O, MgO, MnO, NiO, Na₂O, Sc₂O₃, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, and combinations thereof.
 3. The method of claim 1, the glass further comprising Y₂O₃.
 4. The method of claim 1, the glass further comprising TiO₂.
 5. The method of claim 1, the glass further comprising HfO₂.
 6. The method of claim 1, the difference between T_(g) and T_(x) being at least 35K.
 7. The method of claim 1, the glass collectively comprising less than 40% by weight of SiO₂, B₂O₃, and P₂O₅.
 8. The method of claim 1, the glass collectively comprising less than 10% by weight of SiO₂, B₂O₃, and P₂O₅.
 9. The method of claim 1, the glass collectively comprising less than 5% by weight of SiO₂, B₂O₃, and P₂O₅.
 10. The method of claim 1, the glass collectively comprising at least 80% by weight of REO-Al₂O₃.
 11. An article prepared according to the method of claim
 1. 12. A method of making an article, comprising: providing a glass in a form comprising particles, beads, microspheres, or fibers; the glass comprising: REO-Al₂O₃—ZrO₂; 0 to less than 20% by weight SiO₂; 0 to less than 20% by weight B₂O₃; and 0 to less than 40% by weight P₂O₅; the glass having a glass transition temperature, T_(g), and a crystallization onset temperature, T_(x), and the difference between T_(g) and T_(x) is at least 25K; heating the glass above the T_(g) such that the particles, beads, microspheres, or fibers coalesce to form a coalesced shape; and cooling the coalesced shape to form the article.
 13. The method of claim 12, the glass further comprising an additional metal oxide selected from the group consisting of BaO, CaO, Cr₂O₃, CoO, Fe₂O₃, GeO₂, HfO₂, Li₂O, MgO, MnO, NiO, Na₂O, Sc₂O₃, SrO, TeO₂, TiO₂, V₂O₃, Y₂O₃, ZnO, and combinations thereof.
 14. The method of claim 12, the glass further comprising Y₂O₃.
 15. The method of claim 12, the glass further comprising TiO₂.
 16. The method of claim 12, the glass further comprising HfO₂.
 17. The method of claim 12, the difference between T_(g) and T_(x) being at least 35K.
 18. The method of claim 12, the glass collectively comprising less than 40% by weight of SiO₂, B₂O₃, and P₂O₅.
 19. The method of claim 12, the glass collectively comprising less than 10% by weight of SiO₂, B₂O₃, and P₂O₅.
 20. The method of claim 12, the glass collectively comprising less than 5% by weight of SiO₂, B₂O₃, and P₂O₅.
 21. The method of claim 12, the glass collectively comprising at least 80% by weight of REO-Al₂O₃—ZrO₂.
 22. An article prepared according to the method of claim
 12. 